鋁型材鍍鈦工藝屬于涂裝工藝，是在傳統(tǒng)鍍鈦工藝的基礎(chǔ)上增加預(yù)鍍和電鍍工藝步驟，鋁型材工藝是將活化后的電鍍件置于鹽水和鹽酸水溶液中進(jìn)行化學(xué)處理，那么如何正確使用工業(yè)鋁型材呢，使用工業(yè)鋁型材應(yīng)注意什么。
The titanium plating process for aluminum profiles belongs to the coating process, which adds pre plating and electroplating process steps to the traditional titanium plating process. The aluminum profile process involves chemically treating the activated electroplating parts in a solution of salt water and hydrochloric acid. So, how to use industrial aluminum profiles correctly and what should be paid attention to when using industrial aluminum profiles.
1，清洗時(shí)應(yīng)使用含有潤(rùn)滑劑或中性洗滌劑的溫水，不允許使用酸性或堿性洗滌劑。
1. Warm water containing lubricants or neutral detergents should be used during cleaning, and acidic or alkaline detergents are not allowed.
2，對(duì)于清洗后的鋁合金型材，較好用優(yōu)質(zhì)的工業(yè)型材面漆保護(hù)蠟對(duì)陽(yáng)極氧化膜進(jìn)行拋光，或均勻噴涂一層丙烯酸樹脂清漆。
2. For cleaned aluminum alloy profiles, it is better to polish the anodic oxide film with high-quality industrial profile paint protective wax, or evenly spray a layer of acrylic resin varnish.
三，運(yùn)輸鋁合金型材時(shí)，嚴(yán)禁松開散裝車，以免造成損壞。
3、 When transporting aluminum alloy profiles, it is strictly prohibited to loosen the bulk truck to avoid damage.
四，清潔工具較好用軟布和毛巾，嚴(yán)禁用剛玉粉，砂紙，鋼絲刷等摩擦材料對(duì)鋁門窗表面進(jìn)行清理。
4、 It is better to use soft cloth and towel as cleaning tools. It is strictly prohibited to use friction materials such as corundum powder, sandpaper, and steel wire brushes to clean the surface of aluminum doors and windows.
5個(gè)，鋁合金門窗應(yīng)根據(jù)使用環(huán)境定期清洗。
5 aluminum alloy doors and windows should be cleaned regularly according to the usage environment.
6，鋁型材表面腐蝕，污染時(shí)，應(yīng)及時(shí)清理，可以先用軟布和酒精擦工業(yè)型材拭積垢，然后用水清洗。
6. When the surface of aluminum profiles is corroded or contaminated, it should be cleaned in a timely manner. You can first use a soft cloth and alcohol to wipe away the scale on the industrial profile, and then clean it with water.
一，熔鑄是工業(yè)鋁材生產(chǎn)的首道工序，主要過程為：。
1、 Melting casting is the first process in industrial aluminum production, and the main process is as follows:.
1，配料：根據(jù)需要生產(chǎn)的具體合號(hào)，計(jì)算出各種合金成分的添加量，合理搭配各種原材料，2，熔煉：將配好的原材料按工藝要求加入熔煉爐內(nèi)熔化，并通過除氣，除渣精煉手段將熔體內(nèi)的雜渣，氣體有效除去。
1. Ingredients: Calculate the addition amount of various alloy components based on the specific alloy grade required for production, and reasonably mix various raw materials. 2. Melting: Add the prepared raw materials to the melting furnace according to the process requirements for melting, and effectively remove impurities and gases from the melt through degassing and slag removal refining methods.
3，鑄造：熔煉好的鋁液在一定的鑄造工藝條件下，通過深井鑄造系統(tǒng)，冷卻鑄造成各種規(guī)格的圓鑄棒。
3. Casting: The melted aluminum liquid is cooled and cast into various specifications of round cast rods through a deep well casting system under certain casting process conditions.
二，擠壓是型材成形的手段，先根據(jù)型材產(chǎn)品斷面設(shè)計(jì)，制造出模具，利用擠壓機(jī)將加熱好的圓鑄棒從模具中擠出成形。
2、 Extrusion is a method of forming profiles. First, a mold is designed based on the cross-section of the profile product, and the heated round cast rod is extruded from the mold using an extruder.
三，工業(yè)鋁型材表面上色，氧化，擠壓好的鋁合金型材，其表面耐蝕性不強(qiáng)，須通過陽(yáng)極氧化進(jìn)行表面處理以增加鋁材的抗蝕性，耐磨性及外表的美觀度，工業(yè)型材。
3、 The surface of industrial aluminum profiles is colored, oxidized, and extruded. The surface corrosion resistance of aluminum profiles is not strong, and surface treatment must be carried out through anodizing to increase the corrosion resistance, wear resistance, and aesthetic appearance of aluminum profiles.